Mold design

The mold consists of two primary components, the injection mold (A plate) and the ejector mold (B plate). These components are 

also referred to as Molder and Moldmaker Plastic resin enters the mold through a sprue or gate in the injection mold; the 

sprue bushing is to seal tightly against the nozzle of the injection barrel of the molding machine and to allow molten plastic to flow 

from the barrel into the mold, also known as the cavity. The sprue bushing directs the molten plastic to the cavity images through 

channels that are machined into the faces of the A and B plates. These channels allow plastic to run along them, so they are 

referred to as runners. The molten plastic flows through the runner and enters one or more specialized gates and into the cavity 

geometry to form the desired part.

 

The amount of resin required to fill the sprue, runner and cavities of a mold is a shot. Trapped air in the mold can escape through 

air vents that are ground into the parting line of the mold, or around ejector pins and slides that are slightly smaller than the holes 

retaining them. If the trapped air is not allowed to escape, it is compressed by the pressure of the incoming material and 

squeezed into the corners of the cavity, where it prevents filling and can also cause other defects. The air can even become so 

compressed that it ignites and burns the surrounding plastic material. 

 

To allow for removal of the molded part from the mold, the mold features must not overhang one another in the direction that the 

mold opens, unless parts of the mold are designed to move from between such overhangs when the mold opens (using 

components called Lifters).Sides of the part that appear parallel with the direction of draw (The axis of the cored position (hole) or 

insert is parallel to the up and down movement of the mold as it opens and closes) are typically angled slightly, called draft, to 

ease release of the part from the mold. Insufficient draft can cause deformation or damage. The draft required for mold release is 

primarily dependent on the depth of the cavity: the deeper the cavity, the more draft necessary. Shrinkage must also be taken into 

account when determining the draft required If the skin is too thin, then the molded part will tend to shrink onto the cores 

that form whilecooling and cling to those cores, or the part may warp, twist, blister or crack when the cavity is pulled away.